On crystal alignment in polycrystalline YBCO materials based on TEM observation

Previously, we have observed that parallel lattice fringes show up regularly in MTG samples, indicative of good alignment of unit cells in strips of size 100 nm × a few times 100 nm. We have prepared films ( 80 nm) for TEM observation using YBCO material fabricated by the conventional solid-state reaction method in order to study the crystal texture in a length scale from a few 100 nm down to 3 Å. Parallel lattice fringes are observed to stretch across a cross-section 0.3×0.5 m². Cross lattice fringes intersecting at 90° and 45° are observed as rare events. This result suggests that the degree of alignment in the crystal texture is higher than expected inside a grain of size a few m.