| 不锈钢在海洋环境中的腐蚀 |
| |
| 引用本文： | 黄桂桥.不锈钢在海洋环境中的腐蚀[J].腐蚀与防护,1999,20(9):392-394,407. |
| |
| 作者姓名： | 黄桂桥 |
| |
| 作者单位： | 钢铁研究总院青岛海洋腐蚀研究所!青岛266071 |
| |
| 基金项目： | 国家自然科学基金资助项目59899140号 |
| |
| 摘 要： | 在海洋大气区含铬大于１７％的不锈钢基本不腐蚀，在飞溅区，在含铬大于１７％的不锈钢腐蚀较轻，耐蚀性没有明显的差别。２Ｃｒ１３在海洋大气区和飞溅区不能维持钝态。不锈钢在潮 汐区的腐蚀较重，耐蚀性有明显差别。不锈钢在全浸区的腐蚀业重，耐蚀性判别很大。海生物污损对不锈钢的腐蚀有明显的影响。
|
| 关 键 词： | 不锈钢 腐蚀 海洋环境 海水腐蚀 |
CORROSION OF STAINLESS STEELS IN MARINE ENVIRONMENT |
| |
| Huang Guiqiao.CORROSION OF STAINLESS STEELS IN MARINE ENVIRONMENT[J].Corrosion & Protection,1999,20(9):392-394,407. |
| |
| Authors: | Huang Guiqiao |
| |
| Abstract: | Stainless steels that have more than 17% Cr showed very good corrosion resistance in marine atmosphere and relatively good corrosion resistance in marine splash zone. 2Crl3 stainless steel could not keep passive state in both marine atmosphere and splash zone. In tidal zone, corrosion of stainless steels were more serious and their corrosion resistance had obvious difference. Stainless steels immersed in seawater corroded seriously and difference of corrosion resistance was very big. Effect of fouling on corrosion of stainless steels was obvious in marine environment. |
| |
| Keywords: | Stainless steel Marine Corrosion |