| Abstract: | A long‐alkane‐segment semicrystalline polyamide based on 1,12‐diaminododecane and 1,12‐dodecanedicarboxylic acid was synthesized and characterized. The polymer was prepared by melt polycondensation. The molecular weight of the material ranged from 20,000 to 40,000 g/mol, depending on the polymerization conditions. The resulting product was characterized by means of elemental analysis, infrared spectrometry, 1H‐ and 13C‐NMR, intrinsic viscosity, differential scanning calorimetry (DSC), thermogravimetric analysis, dynamic mechanical analysis, and wide‐angle X‐ray diffraction (WAXD). Some mechanical properties were measured. In addition, the thermal behavior of nylon 12,14 was systematically investigated with DSC and variable‐temperature WAXD. Double endotherms were observed during the melting of the polymer, which might have originated from the melt and recrystallization processes of nylon 12,14 on heating. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 88: 1581–1589, 2003 |