Microstructure variation effects on room temperature fatigue threshold and crack propagation in Udimet 720Li Ni-base superalloy
Authors:H T PANG  P A S REED
Affiliation:Materials Research Group, School of Engineering Sciences, University of Southampton, Highfield, Southampton SO17 1BJ, UK;, Department of Materials Science &Metallurgy, University of Cambridge, Pembroke Street, Cambridge CB2 3QZ, UK
Abstract:An assessment of the effects of microstructure on room temperature fatigue threshold and crack propagation behaviour has been carried out on microstructural variants of U720Li, i.e. as‐received U720Li, U720Li‐LG (large grain variant) and U720Li‐LP (large intragranular coherent γ′ variant). Fatigue tests were carried out at room temperature using a 20 Hz sinusoidal cycling waveform at an R‐ratio = 0.1 on 12.5 mm × 12.5 mm square cross‐section SENB specimens with a 60° starter notch. U720Li‐LG showed the highest threshold ΔKKth), whilst U720Li‐LP showed the lowest ΔKth value. U720Li‐LP also showed higher crack growth rates in the near‐threshold regime and at high ΔK (although at higher ΔK levels the difference was less marked). Crack growth rates of U720Li and U720Li‐LG were relatively similar both in the near‐threshold regime and at high ΔK. The materials showed crystallographic stage I type crack growth in the near‐threshold regime, with U720Li showing distinct crystallographic facets on the fracture surface, while U720Li‐LG and U720Li‐LP showed mostly microfacets and a lower proportion of large facets. At high ΔK, crack growth in the materials becomes flat and featureless indicative of stage II type crack growth. The observed fatigue behaviour, which is an effect of the combined contributions of intrinsic and extrinsic crack growth resistances, is rationalized in terms of the microstructural characteristics of the materials. Enhanced room temperature fatigue threshold and near‐threshold long crack growth resistance are seen for materials with larger grain size and higher degree of planar slip which may be related to increased extrinsic crack growth resistance contributions from crack tip shielding and roughness‐induced crack closure. Differences in the deformation behaviour, either homogeneous or heterogeneous due to microstructural variation in this set of materials may provide approximately equivalent intrinsic crack growth resistance contributions at room temperature.
Keywords:fatigue crack propagation  fatigue threshold  microstructural effects  Udimet 720Li
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号