| Abstract: | The preparation of a SiC coating on a carbon fiber surface using a sol-gel mixture of tetraethyl orthosilicat (TEOS) and phenolic resin was studied. FTIR and SEM investigations indicated that the SiC coating can be formed by carbothermal reduction of the sol-gel mixture at 1420°C for 15–20 min in an argon atmosphere. TGA of the coated fiber was also performed, showing that the SiC coating improves the thermooxidative stability of the carbon fiber. With the thickness of the obtained coating of 0.47 μm using a C/Si ratio of 4, this treatment does not affect the carbon fiber strength. |