Effect of prior austenitic grain boundary composition on temper brittleness in a Ni-Cr-Sb steel

Grain boundary segregation during temper embrittlement of an Sb-containing, Ni-Cr steel has been examined both by Auger electron analysis and by chemical analysis by neutron activation of residues of surface layers dissolved by etching intercrystalline fracture surfaces. No grain boundary segregation of either alloying additions or impurities was detected during austenitization or tempering. Redistribution of Cr, Ni, and Sb between carbide and ferrite was observed during tempering, but no grain boundary segregation was noted. Both Ni and Sb were observed to segregate to the boundaries during embrittling. The segregated Sb was shown to be uniformly distributed along the prior austenitic grain boundaries and to control the ductile brittle transition temperature of the alloy studied. Ni segregating to the prior austenitic boundaries during embrittling was shown to be localized in a phase other than the ferritic portions of the boundaries. A possible location was shown to be the ferritecarbide interfaces in the grain boundaries. Weakening of these normally tenacious carbide and ferrite interfaces could account for the change in mode of brittle failure from transcrystalline cleavage to intercrystalline along the prior austenitic grain boundaries that is observed in temper brittle steels.