Reforming of bioethanol over Ni/Al2O3 and Ni/CeZrO2/Al2O3 catalysts in supercritical water for hydrogen production

Bioethanol was reformed in supercritical water (SCW) at 500 °C and 25 MPa on Ni/Al₂O₃ and Ni/CeZrO₂/Al₂O₃ catalysts to produce high-pressure hydrogen. The results were compared with non-catalytic reactions. Under supercritical water and in a non-catalytic environment, ethanol was reformed to H₂, CO₂ and CH₄ with small amounts of CO and C2 gas and liquid products. The presence of either Ni/Al₂O₃ or Ni/CeZrO₂/Al₂O₃ promoted reactions of ethanol reforming, dehydrogenation and decomposition. Acetaldehyde produced from the decomposition of ethanol was completely decomposed into CH₄ and CO, which underwent a further water-gas shift reaction in SCW. This led to great increases in ethanol conversion and H₂ yield on the catalysts of more than 3-4 times than that of the non-catalytic condition. For the catalytic operation, adding small amounts of oxygen at oxygen to ethanol molar ratio of 0.06 into the feed improved ethanol conversion, at the expense of some H₂ oxidized to water, resulting in a slightly lower H₂ yield. The ceria-zirconia promoted catalyst was more active than the unpromoted catalyst. On the promoted catalyst, complete ethanol conversion was achieved and no coke formation was found. The ceria-zirconia promoter has important roles in improving the decomposition of acetaldehyde, the enhancement of the water-gas shift as well as the methanation reactions to give an extremely low CO yield and a tremendously high H₂/CO ratio. The SCW environment for ethanol reforming caused the transformation of gamma-alumina towards the corundum phase of the alumina support in the Ni/Al₂O₃ catalyst, but this transformation was slowed down by the presence of the ceria-zirconia promoter.