| NaY分子筛模板法合成多孔炭材料 |
| |
| 引用本文： | 伍刚,李德伏,王金渠. NaY分子筛模板法合成多孔炭材料[J]. 材料科学与工程学报, 2006, 24(4): 565-567 |
| |
| 作者姓名： | 伍刚 李德伏 王金渠 |
| |
| 作者单位： | 大连理工大学吸附与无机膜研究所,辽宁,大连,116012;大连理工大学吸附与无机膜研究所,辽宁,大连,116012;大连理工大学吸附与无机膜研究所,辽宁,大连,116012 |
| |
| 摘 要： | 采用NaY沸石分子筛作模板,乙酰丙酮为炭前驱体,使用液相浸渍-气相沉积工艺合成了富含微孔和中孔结构的多孔炭材料并对其进行了表征.所合成的多孔炭比表面积1351m2/g,孔容0.892cm3/g,微孔率0.63,孔径分布多在0.8nm～3.0nm之间.
|
| 关 键 词： | 多孔炭 模板 沸石 乙酰丙酮 |
| 文章编号： | 1673-2812(2006)04-0565-03 |
| 修稿时间： | 2005-10-05 |
Preparation of Porous Carbon Using Zeolite NaY as Template |
| |
| WU Gang,LI De-fu,WANG Jin-qu. Preparation of Porous Carbon Using Zeolite NaY as Template[J]. Journal of Materials Science and Engineering, 2006, 24(4): 565-567 |
| |
| Authors: | WU Gang LI De-fu WANG Jin-qu |
| |
| Abstract: | Porous carbon with controlled pore size distributions between 0.8nm and 3.0nm were synthesized by using zeolite NaY as a template.Acetylacetone was employed as a carbon precursor to prepare porous carbons by impregnation method and chemical vapor deposit method.The porous carbon prepared exhibited two kinds of pore structure:microporus and mesoporous,with surface area,microporisity and micropore volume reaching 1351m~2/g,0.63 and 0.892cm~3/g respectively. |
| |
| Keywords: | porous carbon template zeolite acetylacetone |