Electroconductive Al2O3–NbN Composites

Electroconductive Al₂O₃–NbN ceramic composites were prepared by hot pressing. Dense sintered bodies of ball-milled Al₂O₃–NbN composite powders were obtained at 1550°C and 30 MPa for 1 h under a nitrogen atmosphere. The bending strength and fracture toughness of the composites were enhanced by incorporating niobium nitride (NbN) particles into the Al₂O₃ matrix. The electrical resistivity of the composites decreased with increasing amount of NbN phase. For a 25 vol% NbN–Al₂O₃ composite, the values of bending strength, fracture toughness, Vickers hardness, and electrical resistivity were 444.2 MPa, 4.59 MPa·m^1/2, 16.62 GPa, and 1.72 × 10^?2Ω·cm, respectively, making the composite suitable for electrical discharge machining.