JR curves of the low alloy steel 20 MnMoNi 5 5 with two different sulphur contents in oxygen-containing high temperature water at 240°C

J_R curves of the low alloy steel 20 MnMoNi 5 5 with two different sulphur contents (0.003 and 0.011 wt.%) were determined at 240°C in oxygen-containing high temperature water as well as in air. The tests were performed by the single-specimen unloading compliance technique at load line displacement rates from 1 × 10⁻⁴ down to 1 × 10⁻⁶ mm s⁻¹ on 20% side-grooved 2T CT specimens in an autoclave testing facility at an oxygen content of 8 ppm and a pressure of 7 MPa under quasi-stagnant flow conditions.In the case of testing in high temperature water, remarkably lower J_R curves than in air at the same load line displacement rate (1 × 10⁻⁴ mm s⁻¹) were obtained. A decrease in the load line displacement rate as well as an increase in the sulphur content of the steel caused a reduction of the J_R curves. At the fastest load line displacement rate a stretch zone could be detected fractographically on the specimens tested in air and in high temperature water and consequently J_i could be determined. When testing in high temperature water, the J_i value of the higher sulphur material type decreases from 45 N mm⁻¹ in air to 3 N mm⁻¹, much more than that of the optimized material type from 51 N mm⁻¹ in air to 20 N mm⁻¹ at 1 × 10⁻⁴ mm s⁻¹.