| 竹碎料板用低毒脲醛树脂的合成工艺研究 |
| |
| 引用本文： | 李国进.竹碎料板用低毒脲醛树脂的合成工艺研究[J].中国胶粘剂,2009,18(8). |
| |
| 作者姓名： | 李国进 |
| |
| 作者单位： | 湖南省农林工业勘察设计研究总院,湖南,长沙,410007 |
| |
| 摘 要： | 在脲醛树脂(UF)的制备过程中,采用三聚氰胺对UF进行改性,制得低毒UF。结果表明:该低毒UF的固含量为49.88%,游离甲醛释放量仅为0.2026%;采用这种低毒UF胶粘剂压制的竹碎料板,其静曲强度为22.6MPa,弹性模量为2056MPa,内结合强度为0.58MPa,2h吸水厚度膨胀率为2.57%;该低毒UF是一种综合性能良好的木材用胶粘剂,其应用前景非常广阔。
|
| 关 键 词： | 竹碎料板 低毒 脲醛树脂 合成工艺 |
Study on synthetic process of low toxic urea-formaldehyde resin for bamboo particleboard |
| |
| LI Guo-jin.Study on synthetic process of low toxic urea-formaldehyde resin for bamboo particleboard[J].China Adhesives,2009,18(8). |
| |
| Authors: | LI Guo-jin |
| |
| Affiliation: | Hunan Prospecting Designing and Research Institute for Agriculture Forest Industry;Changsha 410007;China |
| |
| Abstract: | A low toxic urea-formaldehyde resin(UF)which was modified by melamine was synthesized in preparing process of UF. The results showed that the solid content was 49.88% and the free formaldehyde content was 0.202 6% for low toxic UF. The statictuneintensity was 22.6 MPa, elastic modulus was 2 056 MPa, interior bonding strength was 0.58 MPa and thickness expanded ratio after absorbing water 2 h was 2.57% for the bamboo particleboard pressed by low toxic UF adhesive. The low toxic UF was an adhesive for wood wi... |
| |
| Keywords: | bamboo particleboard low toxic urea-formaldehyde resin(UF) synthetic process |