The effect of CeO2 structure on the activity of supported Pd catalysts used for methane steam reforming

Palladium (Pd) supported on CeO₂-promoted γ-Al₂O₃ with various CeO₂ (ceria) crystallinities, were used as catalysts in the methane steam reforming reaction. X-ray diffraction (XRD) analysis, FTIR spectroscopy of adsorbed CO, and X-ray photoelectron spectroscopy (XPS) were employed to characterize the samples in terms of Pd and CeO₂ structure and dispersion on the γ-Al₂O₃ support. These results were correlated with the observed catalytic activity and deactivation process. Arrhenius plots at steady-state conditions are presented as a function of CeO₂ structure. Pd is present on the oxidized CeO₂-promoted catalysts as Pd⁰, Pd⁺ and Pd²⁺, at ratios strongly dependent on CeO₂ structure. XRD measurements indicated that Pd is well dispersed (particles <2 nm) on crystalline CeO₂ and is agglomerated as large clusters (particles in 10–20 nm range) on amorphous CeO₂. FTIR spectra of adsorbed CO revealed that after pre-treatment under H₂ or in the presence of amorphous CeO₂, partial encapsulation of Pd particles occurs. CeO₂ structure influences the CH₄ steam reforming reaction rates. Crystalline CeO₂ and dispersed Pd favor high reaction rates (low activation energy). The presence of CeO₂ as a promoter conferred high catalytic activity to the alumina-supported Pd catalysts. The catalytic activity is significantly lower on Pd/γ-Al₂O₃ or on amorphous (reduced) CeO₂/Al₂O₃ catalysts. The reaction rates are two orders of magnitude higher on Pd/CeO₂/γ-Al₂O₃ than on Pd/γ-Al₂O₃, which is attributed to a catalytic synergism between Pd and CeO₂. The low rates on the reduced Pd/CeO₂/Al₂O₃ catalysts can be correlated with the loss of Pd sites through encapsulation or particle agglomeration, a process found mostly irreversible after catalyst regeneration.