Ageing of Mg–Ni–H hydrogen storage alloys

In this work, ageing of Mg/Mg₂Ni mixtures was investigated. It was observed that hydrogen desorption kinetics from hydrided Mg/Mg₂Ni was improved considerably after ageing at room temperature for several days. The ageing was interpreted in terms of phase changes. Even after almost complete hydridation, besides two main phases – MgH₂ and Mg₂NiH₄ – a certain amount of Mg₂NiH_0.3 was always present. Similar as Mg₂NiH₄ phase, Mg₂NiH_0.3 islands were located on the surface of MgH₂ grains. Mg₂NiH_0.3 transformed into Mg₂NiH₄ at the expense of hydrogen from an adjoining MgH₂ grain. In such a way, a clean double layer (Mg)–Mg₂NiH₄ was formed, acting as a gate for easy hydrogen desorption from MgH₂. It was found that the Mg₂NiH₄ phase was slightly enriched on non-twinned modification LT1 during the ageing. As a result, both the creation of (Mg)–Mg₂NiH₄ desorption bridges and enrichment of Mg₂NiH₄ on LT1 during the ageing facilitated onset of rapid hydrogen desorption.