Hydrogen sorption in MgH2-based composites: The role of Ni and LiBH4 additives

In the present work we investigate the hydrogen sorption properties of composites in the MgH₂–Ni, MgH₂–Ni–LiH and MgH₂–Ni–LiBH₄ systems and analyze why Ni addition improve hydrogen sorption rates while LiBH₄ enhance the hydrogen storage capacity. Although all composites with Ni addition showed significantly improved hydrogen storage kinetics compared with the pure MgH₂, the fastest hydrogen sorption kinetics is obtained for Ni-doped MgH₂. The formation of Mg₂Ni/Mg₂NiH₄ in Ni-doped MgH₂ composite and its microstructure allows to uptake 5.0 wt% of hydrogen in 25 s and to release it in 8 min at 275 °C. In the MgH₂–Ni–LiBH₄ composite, decomposition of LiBH₄ occurs during the first dehydriding leading to the formation of diborane, which has a Ni catalyst poison effect via the formation of a passivating boron layer. A combination of FTIR, XRD and volumetric measurements demonstrate that the formation of MgNi₃B₂ in the MgH₂–Ni–LiBH₄ composite happens in the subsequent hydriding cycle from the reaction between Mg₂Ni/Mg₂NiH₄ and B. Activation energy analysis demonstrates that the presence of Ni particles has a catalytic effect in MgH₂–Ni and MgH₂–Ni–LiH systems, but it is practically nullified by the addition of LiBH₄. The beneficial role of LiBH₄ on the hydrogen storage capacity of the MgH₂–Ni–LiBH₄ composite is discussed.