纳米CaCO3增强增韧聚乙烯母粒的开发与应用

介绍了一种将纳米CaCO3填充到LDPE中制成母粒,应用到节水滴灌输水软管中的工艺.实验证明纳米CaCO3对PE输水软管有着明显的增韧增强效果,添加量达到8%时,软管缺口冲击强度达到最大值58.9 kJ/m2,拉伸强度与断裂伸长率也同时达到最大值,分别为43.62MPa和824.8%,并且加工时可使树脂的流动速率增加,显著提高生产效率,降低生产成本,有很强的现实意义.

Development and Application of Nano-CaCO3 Reinforced and Toughened Polyethylene Masterbatch

The introduction was made on a kind of technique of making masterbatch by filling nano-CaCO_3 into LDPE and preparing watersaving hose for drip irrigation.The experiment proved nano-CaCO_3 had obvious reinforcing and toughening effect on the hose of PE.When the nano-CaCO_3 content was 8%,the notched impact strength was up to maximum of 58.9 kJ/m~2,the tensile strength and elongation at break were up to maximum of 43.62MPa and 824.8% respectively.Nano-CaCO_3 can increase the flow speed of the resin while processing,improve producing efficiency notably,and reduce production cost.The technique has a strong realistic significance.