Preparation and physical properties of transparent organic–inorganic nanohybrid materials based on urethane dimethacrylate

The aim of this study was to prepare transparent organic–inorganic nanohybrid materials with improved physical properties in comparison with the matrix polymer. Polymerizable silica nanoparticles were synthesized via the reaction of silanol groups on the surface of silica nanoparticles (particle diameter ≈ 12 nm) with isocyanate groups of 2‐(methacryloyloxy)ethyl isocyanate (MOI) in ethyl acetate. In addition, the matrix monomer, urethane dimethacrylate, was prepared by the reaction of an MOI isocyanate group with the hydroxyl group of 2‐hydroxyethyl methacrylate, and novel organic–inorganic nanohybrid materials were obtained at various silica contents with bulk polymerization. The surface treatment of the silica nanoparticles and preparation of the matrix monomer were carried out in a one‐pot reaction. The prepared hybrid materials retained high transparency, and the elastic modulus and surface hardness improved with increasing silica content. Moreover, the strength of the material containing 20 wt % silica was up to 30 MPa higher than that of the matrix polymer. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008