Complex structural contribution of the morphotropic phase boundary in Na0.5Bi0.5TiO3 - CaTiO3 system

The correlation between structure and dielectric properties of lead-free (1-x)Na_0.5Bi_0.5TiO₃ - xCaTiO₃ ((1-x)NBT - xCT) polycrystalline ceramics was investigated systematically by X-ray diffraction, combined with impedance spectroscopy for dielectric characterizations. The system shows high miscibility in the entire composition range. A morphotropic phase boundary (MPB), at 0.09?≤?x?<?0.15 was identified where rhombohedral and orthorhombic symmetries coexist at room temperature. The fraction of orthorhombic phase increases gradually with x in the MPB region. Dielectric measurements reveal that the relative permittivity increase with addition of Ca²⁺. This behavior is unusual with this kind of doping. A thermal hysteresis occurred only in the MPB composition which varies in a non-monotonically manner with x, detected by dielectric properties. This phenomenon is related to the crystalline microstructure by a linear relationship between the fraction of each phase and dielectric properties, and, more precisely, to the strong interaction between rhombohedral and orthorhombic phases.