环氧树脂/POSS杂化材料力学性能和耐热性研究 |
| |
引用本文: | 辛存良马晓燕宋春莹侯宪冰屈小红. 环氧树脂/POSS杂化材料力学性能和耐热性研究[J]. 中国塑料, 2012, 26(9): 52-55. DOI: 10.19491/j.issn.1001-9278.2012.09.011 |
| |
作者姓名: | 辛存良马晓燕宋春莹侯宪冰屈小红 |
| |
作者单位: | 西北工业大学理学院应用化学系西北工业大学理学院应用化学系西北工业大学理学院应用化学系西北工业大学理学院应用化学系 |
| |
摘 要: | 以自行合成的环氧基倍半硅氧烷(POSS)为改性剂,分别对环氧树脂139S/六氢苯酐和环氧树脂BE 188EL/六氢苯酐进行改性,制备环氧树脂/POSS杂化材料。力学性能分析结果表明,两种杂化材料的冲击强度和弯曲强度都有明显的提高,冲击强度分别提高了57.45 %和32.26 %,弯曲强度分别提高了9.23 %和5.07 %。热性能分析结果表明,两种杂化材料在高温时的热残留量都有所提高,分别提高了50.19 %和20.16 %。两种杂化材料的热膨胀系数也得到了降低,即热稳定性得到了提高。
|
关 键 词: | 环氧树脂 笼形倍半硅氧烷 力学性能 热性能 热膨胀系数 |
收稿时间: | 2012-05-22 |
Study on Mechanical Properties and Thermal Stability on |
| |
Abstract: | Two epoxy resin systems (139S and BE 188EL cured with hexahydrophthalic anhydride) were modified with 3 glycidoxypropyl polyhedral oligomeric silsesquioxane cage (POSS) led to POSS/epoxy hybrid materials. The impact strengths of the two epoxy systems were increased by 57.45 % and 32.26 %, the flexural strength were increased by 9.23 % and 5.07 %,and the thermal residual weight increased by 50.19% and 20.16%. Meanwhile, the coefficients of thermal expansion was lowered. |
| |
Keywords: | epoxy resin polyhedral oligomeric silsequioxane mechanical properties thermal stability coefficient of thermal expansion |
|