MOS devices with tetragonal ZrO2 as gate dielectric formed by annealing ZrO2/Ge/ZrO2 laminate

A Ge-stabilized tetragonal ZrO₂ (t-ZrO₂) film with permittivity (κ) of 36.2 was formed by depositing a ZrO₂/Ge/ZrO₂ laminate and a subsequent annealing at 600 °C, which is a more reliable approach to control the incorporated amount of Ge in ZrO₂. On Si substrates, with thin SiON as an interfacial layer, the SiON/t-ZrO₂ gate stack with equivalent oxide thickness (EOT) of 1.75 nm shows tiny amount of hysteresis and negligible frequency dispersion in capacitance-voltage (C-V) characteristics. By passivating leaky channels derived from grain boundaries with NH₃ plasma, good leakage current of 4.8 × 10⁻⁸ A/cm² at V_g = V_fb − 1 V is achieved and desirable reliability confirmed by positive bias temperature instability (PBTI) test is also obtained.