Characterization of anodic coating formed on Mg-3Nd-0.2Zn-0.4Zr Mg alloy in alkaline electrolyte |
| |
| Authors: | CHANG Jian-wei GUO Xing-wu PENG Li-ming DING Wen-jiang PENG Ying-hong National Engineering Research Center of Light Alloys Net Forming School of Materials Science Engineering Shanghai Jiao Tong University Shanghai China School of Mechanical Engineering |
| |
| Affiliation: | CHANG Jian-wei,GUO Xing-wu,PENG Li-ming,DING Wen-jiang,PENG Ying-hong 1.National Engineering Research Center of Light Alloys Net Forming(LAF),School of Materials Science , Engineering,Shanghai Jiao Tong University,Shanghai 200240,China,2.School of Mechanical Engineering |
| |
| Abstract: | Anodization of rare earth-containing Mg alloy of Mg-3Nd-0.2Zn-0.4Zr(mass fraction,%)(NZ30K)was performed in composite electrolyte containing NaOH,KOH,K2SiO3,Na2SiO3,NaF,KF etc.The anodic coating was characterized by using X-ray diffraction(XRD),field emission electron scanning microseope(FE-SEM)and electron probe microscopic analysis(EPMA).The corrosion resistance of the anodized alloy and the substrate was evaluated in 5%NaCl solution using electrochemical impedance spectroscopy(EIS).The results of XRD show that the anodic coating is mainly composed of MgO.EPMA indicates that magnesium and oxygen are almost uniformly distributed across the coating,and the fluorine content decreases gradually from the interface of coating-substrate to the surface,whereas the distribution of silicon is reverse to that of fluorine.The results of EIS analysis shows that the anodic coating exhibits the superior corrosion resistance for NZ30K alloy. |
| |
| Keywords: | Mg-Nd-Zn-Zr alloy anodizing corrosion resistance |
| 本文献已被 CNKI 万方数据 等数据库收录！ |
|