| 镗床类立柱裂纹防止措施 |
| |
| 引用本文： | 韩亚伟,张继波,毛春建.镗床类立柱裂纹防止措施[J].现代铸铁,2009(2). |
| |
| 作者姓名： | 韩亚伟 张继波 毛春建 |
| |
| 作者单位： | 沈阳机床银丰铸造有限公司,辽宁,沈阳,110200 |
| |
| 摘 要： | 介绍了铸件产生裂纹的原因以及热裂纹和冷裂纹的特征,分析了镗床类立柱裂纹产生的原因,以其形貌特征认定其为热裂纹。从铸件结构、制芯工艺、熔炼过程和开箱落砂时间方面进行了改进,立柱铸件裂纹缺陷得到了有效的控制。
|
| 关 键 词： | 立柱铸件 裂纹缺陷 防止措施 |
Measures to Prevent Cracking Defects of Boring Machine Columns |
| |
| HAN Ya-wei,ZHANG Ji-bo,MAO Chun-jian.Measures to Prevent Cracking Defects of Boring Machine Columns[J].Modern Cast Iron,2009(2). |
| |
| Authors: | HAN Ya-wei ZHANG Ji-bo MAO Chun-jian |
| |
| Affiliation: | HAN Ya-wei; ZHANG Ji-bo; MAO Chun-jian(Yinfeng Foundry Co.; Ltd.; Shenyang Machine Tool Co.; Shenyang 110200; China); |
| |
| Abstract: | The formation reason of casting cracks and the features of both the hot tearing and cold cracking was introduced.The reason causing the cracks of boring machine column was analyzed and it was confirmed according to the morphology of the crack that the defect is hot tearing.Appropriate improvements were adopted to the casting configuration,core-making process,melting process and shakeout time control.As a result,the crack defect has been controlled effectively. |
| |
| Keywords: | column castings crack defect preventive measures |