| 超顺磁性羟基磷灰石/壳聚糖棒材的制备 |
| |
| 引用本文： | 陈福平,胡巧玲,伍佳,沈家骢. 超顺磁性羟基磷灰石/壳聚糖棒材的制备[J]. 材料研究学报, 2006, 20(3): 250-254 |
| |
| 作者姓名： | 陈福平 胡巧玲 伍佳 沈家骢 |
| |
| 作者单位： | 浙江大学高分子复合材料研究所,杭州,310027;浙江大学高分子复合材料研究所,杭州,310027;浙江大学高分子复合材料研究所,杭州,310027;浙江大学高分子复合材料研究所,杭州,310027 |
| |
| 基金项目： | 国家自然科学基金;国家研究发展基金 |
| |
| 摘 要： | 以壳聚糖膜为模板将磁性羟基磷灰石前驱体的壳聚糖醋酸溶液与NaOH凝固液隔离，OH^-向磁性羟基磷灰石前驱体的壳聚糖醋酸溶液内部的渗透引起pH值变化，导致质子化的壳聚糖在模板上沉积的同时无机物就地生成，原位复合制备出无机纳米颗粒分散均匀的磁性羟基磷灰石／壳聚糖（HA／CS）复合棒材．生成的超顺磁性四氧化三铁和羟基磷灰石颗粒大小均一（大约长30nm，宽20nm），在基质中分布均匀、没有出现明显的团聚现象．
|
| 关 键 词： | 复合材料 壳聚糖 磁性羟基磷灰石 原位复合法 棒材 |
| 文章编号： | 1005-3093(2006)03-0250-05 |
| 收稿时间： | 2005-06-10 |
| 修稿时间： | 2006-03-20 |
Preparation of superparamagnetic hydroxyapatite/chitosan rod |
| |
| CHEN Fuping,HU Qiaoling,WU Jia,SHEN Jiacong. Preparation of superparamagnetic hydroxyapatite/chitosan rod[J]. Chinese Journal of Materials Research, 2006, 20(3): 250-254 |
| |
| Authors: | CHEN Fuping HU Qiaoling WU Jia SHEN Jiacong |
| |
| Affiliation: | Institute of Polymer Composites, Zhejiang University, Hangzhou310027. |
| |
| Abstract: | The superparamagnetic hydroxyapatite/chitosan precursory solution was segregated from NaOH solution by using chitosan membrane as template. The pH value was changed tardily due to the penetration of OH~- into this precursory solution, which resulted in the aggradations of chitosan and inorganic particles at the same time. Thus, superparamagnetic hydroxyapatite/chitosan rods were prepared via in-situ compositing. X-ray diffraction was performed to determine the formations of magnetite and hydroxyapatite. Transmission electron microscope was carried out to investigate the magnetite and hy-droxyapatite particles in the chitosan matrix. The results showed that the formation of superparamagnetic magnetite and hydroxyapatite with the maximum size under 30 nm (length about 30 nm, width about 20 nm), which were dispersed homogeneously in the chitosan matrix. |
| |
| Keywords: | composite chitosan magnetic hydroxyapatite in-situ compositing rod |