Rheocasting of semi-solid Al359/20%SiC metal matrix composite using SEED process

A Duralcan Al359/20%SiC metal matrix composite was successfully cast using the SEED rheocasting process. Effects of the SEED processing parameters on the microstructure of semi-solid slurries and casting parts were studied. The parameters investigated in this study include pouring temperature, swirling time and swirling speed. The results showed that α-Al grains were nearly spherical and SiC particles were well distributed in both semi-solid slurries and cast parts when using the appropriate SEED parameters. The mechanical properties of the semi-solid cast components under as cast and T6 conditions were also investigated. Results revealed that a significant improvement of tensile properties was achieved when compared to the conventional gravity castings and those obtained from other semi-solid process.

Le composite Duralcan Al359/20%SiC à matrice métallique a été moulé avec succès en utilisant le procédé de rhéomoulage SEED. L’effet des paramètres du traitement SEED sur la microstructure des pâtes semi-solides et sur les pièces moulées a été étudié. Les paramètres examinés dans cette étude incluaient la température de coulée, ainsi que la durée et la vitesse de rotation. Les résultats ont montré que les grains d’Al-α étaient presque sphériques et que les particules de SiC étaient bien distribuées tant dans les pâtes semi-solides que dans les pièces moulées lorsqu’on utilisait les paramètres appropriés de SEED. On a également examiné les propriétés mécaniques des composantes moulées semi-solides à l’état brut de coulée et sous la condition T6. Les résultats ont révélé une amélioration significative des propriétés de traction par rapport aux moulages conventionnels de coulée par gravité et par rapport aux propriétés obtenues avec d’autres procédés semi-solides.