Ultrafast Formation of Amorphous Bimetallic Hydroxide Films on 3D Conductive Sulfide Nanoarrays for Large‐Current‐Density Oxygen Evolution Electrocatalysis |
| |
Authors: | Xu Zou Yipu Liu Guo‐Dong Li Yuanyuan Wu Da‐Peng Liu Wang Li Hai‐Wen Li Dejun Wang Yu Zhang Xiaoxin Zou |
| |
Affiliation: | 1. State Key Laboratory of Inorganic Synthesis and Preparative Chemistry, College of Chemistry, Jilin University, Changchun, P. R. China;2. Key Laboratory of Bio‐Inspired Smart Interfacial Science and Technology of Ministry of Education, School of Chemistry and Environment, Beihang University, Beijing, P. R. China;3. International Research Center for Hydrogen Energy, Kyushu University, Fukuoka, Japan;4. Department of Chemistry, Tsinghua University, Beijing, P. R. China |
| |
Abstract: | Developing nonprecious oxygen evolution electrocatalysts that can work well at large current densities is of primary importance in a viable water‐splitting technology. Herein, a facile ultrafast (5 s) synthetic approach is reported that produces a novel, efficient, non‐noble metal oxygen‐evolution nano‐electrocatalyst that is composed of amorphous Ni–Fe bimetallic hydroxide film‐coated, nickel foam (NF)‐supported, Ni3S2 nanosheet arrays. The composite nanomaterial (denoted as Ni‐Fe‐OH@Ni3S2/NF) shows highly efficient electrocatalytic activity toward oxygen evolution reaction (OER) at large current densities, even in the order of 1000 mA cm?2. Ni‐Fe‐OH@Ni3S2/NF also gives an excellent catalytic stability toward OER both in 1 m KOH solution and in 30 wt% KOH solution. Further experimental results indicate that the effective integration of high catalytic reactivity, high structural stability, and high electronic conductivity into a single material system makes Ni‐Fe‐OH@Ni3S2/NF a remarkable catalytic ability for OER at large current densities. |
| |
Keywords: | composite materials large current density oxygen evolution reaction electrocatalysis |
|
|