| 钼对0Cr15Ni5Cu2Ti钢固溶强度的影响 |
| |
| 引用本文： | 叶冰.钼对0Cr15Ni5Cu2Ti钢固溶强度的影响[J].特钢技术,2006,11(2):29-31. |
| |
| 作者姓名： | 叶冰 |
| |
| 作者单位： | 叶冰（攀钢集团四川长城特殊钢股份有限公司） |
| |
| 摘 要： | 从理论和实践两方面阐述钼对0Cr15Ni5Cu2W钢固溶强度的影响，总结出提高钼含量是解决0Cr15Ni5Cu2Ti钢固溶强度偏低的有效方法。试验结果表明，残钼在0．20％-0．25％之间提高该钢固溶强度作用明显。
|
| 关 键 词： | 钼含量 0Cr15Ni5Cu2Ti钢 固溶强度 提高 |
| 收稿时间： | 2006-02-10 |
| 修稿时间： | 2006年2月10日 |
Effect of Molybdenum on Solid Solution Strength of Steel OCr15NiCu2Ti |
| |
| Ye Bin Co. Ltd. ; Pangang Group.Effect of Molybdenum on Solid Solution Strength of Steel OCr15NiCu2Ti[J].Special Steel Technology,2006,11(2):29-31. |
| |
| Authors: | Ye Bin Co Ltd ; Pangang Group |
| |
| Affiliation: | Sichuan Changcheng Special Steel (Group |
| |
| Abstract: | Effect of Molybdenum on solid solution strength of steel OCr15Ni5Cu2Ti was expounded from two aspects of theory and practice , it is obtained that increasing content of Molybdenum is the effective approach to solve the problem of lower solution strength of steel OCr15NiSCu2Ti . The test result showed that solid solution strength could be obviously increased when residual molybdenum was between 0.20% and 0.25% |
| |
| Keywords: | Molybdenum content 0Cr15Ni5Cu2Ti Solution strength Increase |