Effect of aluminum on microstructure,mechanical properties and pitting corrosion resistance of ultra-pure 429 ferritic stainless steels

Effect of aluminum on microstructure, mechanical properties and pitting corrosion resistance of ultra-pure 429 ferritic stainless steels has been investigated. Aluminum can significantly increase the ratio of equiaxed crystal grains, but the promotion effect has great relation with aluminum content. Aluminum can stabilize ferrite phase and significantly reduce recrystallization temperature. Increased aluminum content can also lead to the precipitate of AlN and Al₂O₃ at higher temperature. The increased amount of AlN may partly contribute to the reduced nitrogen element to form austenite at high temperature, hence the high temperature phase transformation of α + γ → α occurs. The fine and large number of Al₂O₃ particles can refine grain size and then promote recrystallization. The highest intensity of γ-fiber texture {1 1 1}〈1 1 2〉 is observed in the steel with 0.19 wt.% aluminum, which can improve the formability of steels. With the increase of aluminum content, the tensile strength increases linearly but the elongation and plastic strain ratio first increase then decrease, the working hardening index varies slightly among the steels. Appearance of Al₂O₃ inclusions with small size and decreased content of MnS benefit pitting corrosion resistance. However, the large dimension Al₂O₃ inclusions have significantly negative influence on pitting corrosion resistance.