Orientation Dependence of Stress Rupture Properties of a Ni-based Single Crystal Superalloy at 760℃ |
| |
基金项目: | sponsored by the National Basic Research Program of China (Grant No. 2010CB631201);the National Natural Science Foundation of China (Grant Nos. 50931004,51171193,50901079) |
| |
摘 要: | The orientation dependence of creep rupture lives of a single crystal superalloy at 760℃/760 MPa was investigated.The orientations of the specimens tested were about 30°away from 001].The results showed that specimens with orientations on the 001]-011] boundary had the longest rupture life.The deformation of these specimen were controlled by a/2110 slip and a few stacking faults with two orientations were observed.On the other hand,specimens with orientations near the 001]-011] boundary or on the 001]-111] boundary showed short rupture lives,and stacking faults with single orientation were observed in these specimens.The rupture properties and the deformation mechanisms were discussed based on the dislocation pattern and the calculated Schmid factors for different specimens.
|
关 键 词: | Single crystal superalloy Stress rupture Orientation |
本文献已被 CNKI 等数据库收录! |