| 碳纳米管传感器检测SF6放电分解组分的实验研究 |
| |
| 引用本文： | 张晓星,刘王挺,唐炬,孟凡生. 碳纳米管传感器检测SF6放电分解组分的实验研究[J]. 电工技术学报, 2011, 0(11): 121-126 |
| |
| 作者姓名： | 张晓星 刘王挺 唐炬 孟凡生 |
| |
| 作者单位： | 重庆大学输配电装备及系统安全与新技术国家重点实验室 |
| |
| 基金项目： | 国家重点基础研究发展计划项目(2009CB724506) |
| |
| 摘 要： | 研制了一种用浓硫酸和浓硝酸修饰,以印制电路板为基底,用于检测SF6局部放电分解组分的碳纳米管传感器。分析了碳纳米管膜的导电模型,并通过真空下传感器的温度特性试验,对修饰前后的碳纳米管传感器的电阻随温度变化的关系进行了分析。在实验室采用SF6放电分解试验装置,用碳纳米管传感器对分解组分进行检测,结果表明用经混酸修饰后的样品制作出的传感器对SF6放电分解组分表现出较好的吸附性。此外,研究了温度对传感器吸附性能的影响,结果表明,温度在85℃时传感器表现出最强的吸附性。
|
| 关 键 词： | 碳纳米管传感器 电学特性 温度 六氟化硫 分解组分 |
Experimental Study of Carbon Nanotubes Gas Sensor Detecting SF6 Partial Discharge Decomposition Components |
| |
| Zhang Xiaoxing Liu Wangting Tang Ju Meng Fansheng. Experimental Study of Carbon Nanotubes Gas Sensor Detecting SF6 Partial Discharge Decomposition Components[J]. Transactions of China Electrotechnical Society, 2011, 0(11): 121-126 |
| |
| Authors: | Zhang Xiaoxing Liu Wangting Tang Ju Meng Fansheng |
| |
| Affiliation: | Zhang Xiaoxing Liu Wangting Tang Ju Meng Fansheng(State Key Laboratory of Power Transmission Equipment & System Security and New Technology Chongqing University Chongqing 400044 China) |
| |
| Abstract: | A kind of carbon nanotubes(CNTs) gas sensor modified by concentrated sulphuric acid and nitrating acid mixtures was developed based on printed circuit board,which was applied to detect sulfur hexafluoride(SF6) partial discharge(PD) decomposition components.Analyzed the conduction and of CNT films,and according to the temperature property test of sensor in vacuum,the relationship between resistance of two sensors and temperature was analyzed.Experiments were conducted for CNTs gas sensor in the laboratory using SF6 gas decomposition component testing device.Test results show that the modified CNTs sensor have good absorbability for SF6 decomposition components.Moreover,The influence of temperature is studied,and the result proves that the sensor showsd the best adsorption at temperature of 85℃. |
| |
| Keywords: | Carbon nanotubes gas sensor electrical properties temperature SF6 decomposition components |