Synthesis and characterization of poly(ethylene terephthalate)/attapulgite nanocomposites

A kind of clay with fibrous morphology, attapulgite (AT), was used to prepare poly (ethylene terephthalate) (PET)/AT nanocomposites via in situ polymerization. Attapulgite was modified with Hexadecyltriphenylphosphonium bromide and silane coupling agent (3‐glycidoxypropltrimethoxysilane) to increase the dispersion of clay particles in polymer matrix and the interaction between clay particles and polymer matrix. FTIR and TGA test of the organic‐AT particles investigated the thermal stability and the loading quantity of organic reagents. XRD patterns and SEM micrographs showed that the organic modification was processed on the surface of rod‐like crystals and did not shift the crystal structure of silicate. For PET/AT nanocomposites, it was revealed in TEM that the fibrous clay can be well dispersed in polymer matrix with the rod‐like crystals in the range of nanometer scale. The diameter of rod‐like crystal is about 20 nm and the length is near to 500 nm. The addition of the clay particles can enhance the thermal stability and crystallization rate of PET. With the addition of AT in PET matrix, the flexural modulus of those composites was also increased markedly. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 103: 1279–1286, 2007