Cover Picture: Low‐Work‐Function Surface Formed by Solution‐Processed and Thermally Deposited Nanoscale Layers of Cesium Carbonate (Adv. Funct. Mater. 12/2007)

The cover shows the structure of an efficient polymer light emitting diode (PLED) and its energy diagram at the interface between aluminum (Al) and a Cs₂CO₃ interfacial layer. It reveals the origin of enhanced electron injection from the Al electrode due to the low work function of a thermally evaporated Cs₂CO₃ layer, as reported on p. 1966 by Jinsong Huang, Zhen Xu, and Yang Yang. Pictures of the white‐ and red‐emitting PLEDs are also shown. Nanostructured layers of Cs₂CO₃ are shown to function very effectively as cathodes in organic electronic devices because of their good electron‐injection capabilities. Here, we report a comprehensive study of the origin of the low work function of nanostructured layers of Cs₂CO₃ prepared by solution deposition and thermal evaporation. The nanoscale Cs₂CO₃ layers are probed by various characterization methods including current–voltage (I–V) measurements, photovoltaic studies, X‐ray photoelectron spectroscopy (XPS), UV photoelectron spectroscopy (UPS), and impedance spectroscopy. It is found that thermally evaporated Cs₂CO₃ decomposes into CsO₂ and cesium suboxides. The cesium suboxides dope CsO₂, yielding a heavily doped n‐type semiconductor with an intrinsically low work function. As a result, devices fabricated using thermally evaporated Cs₂CO₃ are relatively insensitive to the choice of the cathode metal. The reaction of thermally evaporated Cs₂CO₃ with Al can further reduce the work function to 2.1 eV by forming an Al–O–Cs complex. Solution‐processed Cs₂CO₃ also reduces the work function of Au substrates from 5.1 to 3.5 eV. However, devices prepared using solution‐processed Cs₂CO₃ exhibit high efficiency only if a reactive metal such as Al or Ca is used as the cathode metal. A strong chemical reaction occurs between spin‐coated Cs₂CO₃ and thermally evaporated Al. An Al–O—Cs complex is formed as a result of this chemical reaction at the interface, and this layer significantly reduces the work function of the cathode. Finally, impedance spectroscopy results prove that this layer is highly conductive.