CO2 Sensing Property of CuO-BaTiO3 Mixed Oxide Film Prepared by Self-Assembled Multibilayer Film as a Precursor

Preparation of CuO-BaTiO₃ mixed oxide thin film by the decomposition of a self-assembled multibilayer film as a molecular template was investigated in this study. Furthermore, CO₂ sensing property of the resultant thin film was investigated as a capacitive type sensor. The self-assembled bilayer film of few 1000 layers thickness can be obtained easily by casting an aqueous suspension consisting of dimethyldihexadecylammoiun bromide (DC1-16), Cu(ClO₄)₂, Ba(TiO(C₂H₄)₂), 2,6-dimetyle-3,5heptadione (DHP), and polyvinyl alcohol. Divalent copper ion (Cu²⁺)) which is associated with 2 DHP molecules was incorporated into the molecular bilayer film and BaTiO₃ precursor exists at the interspace of molecular bilayer film by coordinating with polyvinyl alcohol. Upquenching the organic-inorganic film at 1173 K leads to the uniform film of CuO-BaTiO₃ oxide mixture. Although operating temperature shifted to higher temperature, the resultant film exhibits the capacitance change upon exposure to CO₂. Consequently, it is concluded that the mixed oxide film of CuO-BaTiO₃ prepared by the decomposition of multibilayer film was also an appropriate capacitive type CO₂ sensor.