Precipitation in rapidly solidified Al-Mn alloys

Precipitation at 450 °C was studied in melt-spun ribbons containing up to 15 wt pct Mn in solid solution in Al. The as-spun ribbons were microsegregation-free at compositions up to 5 wt pct Mn, but in more concentrated alloys a cellular microstructure was present. Upon annealing, four precipitate phases are observed, some of them being found preferentially on cell boundaries and others being found within the cells. Al₆Mn, G, and the Gℍ phase can coexist for long times at 450 °C, but the G phase appears to be slightly more stable. A less stable T phase was detected in Al-5 wt pct Mn foils following short annealing periods. The supersaturation of the Al matrix can persist for many hours in alloys containing up to 3 wt pct Mn, but is essentially gone after 1 hour in alloys with 5 wt pct Mn or more. On leave at the Center for Materials Research, The Johns Hopkins University, Baltimore, MD 21218. R.J.