| 有机复合绝缘子用耐酸性拉挤电绝缘芯棒 | |
| 引用本文： | 陈平,陈辉,刘丽丽,朱兴松.有机复合绝缘子用耐酸性拉挤电绝缘芯棒[J].复合材料学报,2003,20(4):96-100. |
| 作者姓名： | 陈平 陈辉 刘丽丽 朱兴松 |
| 作者单位： | 1. 大连理工大学,高分子材料系,大连,116012;哈尔滨理工大学,材料科学与工程学院,哈尔滨,150040 2. 哈尔滨玻璃钢研究院,哈尔滨,150036 3. 哈尔滨理工大学,材料科学与工程学院,哈尔滨,150040 |
| 基金项目： | 哈尔滨市重点科技攻关项目(0011211109) |
| 摘 要： | 采用丙烯酸改性酚醛环氧树脂,并对以此树脂为基体,以DDSA为增韧剂研制成功一种耐酸性玻璃钢拉挤电绝缘芯棒用树脂基体配方。应用DSC、TGA和FT-IR等分析技术对该改性树脂基体的固化反应进行了研究,对其浇铸体以及玻璃纤维增强的拉挤芯棒的耐酸性、耐热性等性能也进行了研究。结果表明:该树脂基体满足拉挤工艺要求,用此树脂基体制得的玻璃钢拉挤芯棒具有优异的耐酸性以及良好的机电热性能。 |
| 关 键 词： | 改性环氧树脂 丙烯酸 增韧 耐酸性复合材料 拉挤电绝缘芯棒 |
| 文章编号： | 1000-3851(2003)04-0096-05 |
| 收稿时间： | 2001-12-25 |
| 修稿时间： | 2002-03-04 |
ORGANIC COMPOSITE USED NOVEL ACID RESISTANT GLASS FIBERREINFORCED EPOXY RESIN MATRIX PULTRUSION INSULANT ROD |
|
| CHEN Ping,CHEN Hui,LIU Lili,ZHU Xingsong.ORGANIC COMPOSITE USED NOVEL ACID RESISTANT GLASS FIBERREINFORCED EPOXY RESIN MATRIX PULTRUSION INSULANT ROD[J].Acta Materiae Compositae Sinica,2003,20(4):96-100. | |
| Authors: | CHEN Ping CHEN Hui LIU Lili ZHU Xingsong |
| Affiliation: | 1. Department of Polymer Science,Dalian University of Technology,Dalian 116012,China; 2. Harbin Fiber Reinforced Plastics Institute, Harbin 150036, China; 3. School of Materials Science and Engineering, Harbin University Science and Technology, Harbin 150040, China |
| Abstract: | By using acrylic acid to modify phenolic epoxy resin, an acid resistant resin matrix formulation for pultrusion insulant rod which was toughened by DDSA was optimized. The curing reaction of the modified epoxy resin system was studied by DSC, TGA and FT-IR. The acid resistance, heat resistance, mechanical and electrical properties of the cured compound epoxy resin (cast) and the glass fiber reinforced epoxy resin matrix pultrusion rod were also studied. Experiments show that the resin matrix was suited for pultrusion, and the properties of the insulant rod are excellent. |
| Keywords: | modified epoxy resin acrylic acid toughening acid resistance composite pult rusion insulant rod |