Electrical Characterization of a Joined Electroceramic, La0.85Sr0.15MnO3

Pieces of saw-cut La_0.85Sr_0.15MnO₃ were joined at 1150° and 1250°C under a compressive stress. The strains to form the joints were ∼0.1. Joints formed by plastic deformation were examined using scanning electron microscopy, and they were indistinguishable from the bulk. The room-temperature direct-current resistivity of the joined pieces was identical to that measured in the bulk material. This indicated that a sound, electrically conducting joint could be formed using plastic deformation (grain-boundary sliding) with little surface preparation.