引　言异丁烷脱氢反应是一个受热力学平衡限制的反应 ,平衡转化率很低 ,若将膜反应器用于该反应 ,则可以通过膜不断地从反应区选择性分离出氢气 ,克服了反应受热力学平衡制约的缺点 ,这样就可降低反应温度和减压程度的要求 ,改善反应的工艺条件 ,从而达到高效和节能的目的 .文献中已分别对钯 /陶瓷复合膜1,2 ]和钯 -钌 (钌的质量分数为 2 % )合金膜3]反应器中的异丁烷脱氢反应进行了初步研究 .前文4 ]已对用改进的化学镀新工艺制备的钯和钯 -银 /陶瓷复合膜进行了表征 ,本文将用钯-银 /陶瓷复合膜反应器进行异丁烷脱氢反应的研究 .本工作…

CATALYTIC DEHYDROGENATION OF ISOBUTANE IN PALLADIUM COMPOSITE MEMBRANE REACTOR

Pd-Ag/ceramic composite membrane, which was prepared by improved electroless plating with osmosis , exhibited higher hydrogen flux,reaching 0.619 mol·s -1 ·m -2 (673 K,Δ p =0.196 MPa). The catalytic dehydrogenation of isobutane in the Pd-Ag/ceramic composite membrane reactor was studied. The effects of various operating parameters,such as reaction temperature, linear velocity of feed gas, linear velocity of purge gas, molar ratio of nitrogen to isobutane in feed gas, and pressure of feed gas on conversion of isobutane were investigated. It was observed that the conversion of isobutane (50.5% at 723 K) in the membrane reactor exceeded the equilibrium conversion (18.8% at 723 K) and that in the fixed-bed reactor (15.5% at 723 K). From experimental results for dehydrogenation of isobutane in the membrane reactor, it was found that when a certain partial pressure of hydrogen was maintained in the reaction-side of the reactor, the formation of accumulative carbon overlayers on the surface of dehydrogenation catalyst and membrane was inhibited to some extent, which reduced the deactivation rate of catalyst and membrane.