| 钢筋混凝土锈蚀损伤原因与防治技术 | |
| 引用本文： | 王海勇,周春雷,柏云.钢筋混凝土锈蚀损伤原因与防治技术[J].中国建材科技,2010(2). |
| 作者姓名： | 王海勇 周春雷 柏云 |
| 作者单位： | 1. 山东宝诚置业有限公司,山东,淄博,255000 2. 总参谋部管理保障部工程指挥部,北京,100088 3. 山东理工大学建筑工程学院,山东,淄博,255049 |
| 摘 要： | 混凝土碳化和氯离子侵入是引起结构中钢筋锈蚀的主要原因。文章分析碳化的发生机理和影响因素,分析混凝土中氯离子的来源和诱发钢筋锈蚀的机理。阐述提高混凝土结构耐久性的措施。 |
| 关 键 词： | 碳化 氯离子 钢筋锈蚀 耐久性 |
Research on reasons and control measures about reinforced concrete damaged by corrosion |
|
| Abstract: | Carbonation and chloride are the most important reasons which caused steel corrosion in concrete structure. The mechanism of carbonation occurrence and effect was analyzed.The chloride in concrete where stemed from and corrosion mechanism was introduced too.The Fick model which proposed the chloride diffusion in concrete was stated.Measures improving concrete structure durability were offered. |
| Keywords: | carbonation chloride steel corrosion durability |