铝锂合金机器人搅拌摩擦焊接头组织和性能 |
| |
引用本文: | 张满当,赵运强,董春林,谭锦红,易耀勇,吴伟. 铝锂合金机器人搅拌摩擦焊接头组织和性能[J]. 焊接学报, 2021, 42(5): 71-76. DOI: 10.12073/j.hjxb.20201120002 |
| |
作者姓名: | 张满当 赵运强 董春林 谭锦红 易耀勇 吴伟 |
| |
作者单位: | 沈阳工业大学,沈阳,110870;广东省科学院中乌焊接研究所,广东省现代焊接技术重点实验室,广州,510651;广东省科学院中乌焊接研究所,广东省现代焊接技术重点实验室,广州,510651;沈阳工业大学,沈阳,110870 |
| |
基金项目: | 广东省重点领域研发计划项目(2019B090921003);广州市产学研协同创新重大专项资助项目(201704030056);广州市科技计划项目(201807010063);广州经济技术开发区国际科技开发项目(2019GH15);广东省科学院引进高层次领军人才专项(2016GDASRC-0203). |
| |
摘 要: | 为降低焊接压力以适应机器人搅拌摩擦焊接的需求,采用小尺寸轴肩,在较低焊接载荷下进行搅拌摩擦焊接试验.?以单位面积焊缝热输入相同为控制原则,研究了搅拌头轴肩尺寸对2?mm厚2060-T8铝锂合金搅拌摩擦焊接过程压力、焊缝成形、接头微观组织及力学性能的影响.?结果表明,随着搅拌头轴肩尺寸的减小,所需焊接压力呈非线性下降,且...
|
关 键 词: | 2060-T8铝锂合金 搅拌摩擦焊 焊接压力 微观组织 力学性能 |
收稿时间: | 2020-11-20 |
Structure and properties of friction stir welding joint of Al-Li alloy |
| |
Affiliation: | 1.Shenyang University of Technology, Shenyang, 110870, China2.China-Ukraine institute of Welding, Guangdong Academy of Sciences, Guangdong Provincial Key Laboratory of Advanced Welding Technology, Guangzhou, 510651, China |
| |
Abstract: | In order to reduce the welding pressure and meet the demand of robot friction stir welding, the friction stir welding test was carried out with small size shoulder and lower welding load. With the same heat input per unit area as the control principle, the effects of the shoulder size of the stirring head on the pressure, weld shape, joint microstructure and mechanical properties of 2 mm thick 2060-T8 Al-Li alloy during friction stir welding were studied. The results show that with the decrease of the shoulder size of the stirring head, the required welding pressure decreases nonlinearly, and the pressure amplitude decreases in the stable welding process. When the size of the shoulder is 4 mm, a large flying edge is formed on the surface of the weld and there are holes in the joint. When the size of the shoulder is larger than 6 mm, the joint with good surface shape and no internal defects can be obtained. When the shoulder size is 6 mm, the welding pressure is 2 800 N, the average grain size of the welding core zone is 0.52 μm, the maximum tensile strength of the joint is 396 MPa, which is 74.1% of that of the base metal, the microhardness is “U” type distribution, the fracture position is the welding core zone, and the fracture mode is ductile-brittle mixed fracture. |
| |
Keywords: | |