| 焊缝金属中针状铁素体晶粒长大行为 |
| |
| 引用本文： | 宋峰雨,周来宏,伦文山,黄增阳,柏祥洋. 焊缝金属中针状铁素体晶粒长大行为[J]. 焊接学报, 2021, 42(5): 23-28. DOI: 10.12073/j.hjxb.20200929003 |
| |
| 作者姓名： | 宋峰雨 周来宏 伦文山 黄增阳 柏祥洋 |
| |
| 作者单位： | 龙岩学院,龙岩, 364012;新余学院,新余, 338004;山东恒源兵器科技股份有限公司,泰安, 271000;衢州市质量技术监督检测中心,衢州, 324000;德国亚琛工业大学,实验分子影像研究所,亚琛,52074 |
| |
| 基金项目： | 国家自然科学基金资助项目(51801022)；江西省教育厅科技项目(GJJ191047)；龙岩学院青年博士科研启动基金资助项目(LB201810). |
| |
| 摘 要： | 以针状铁素体(AF)组织为基体组织的大热输入焊缝金属作为研究对象,采用金相显微镜(OM)、扫描电子显微镜电子背散射衍射装置(EBSD)、全自动静态相变仪等手段表征了焊缝金属内细长状的针状铁素体(AF)组织晶粒的取向特征,分析不同焊接热输入对焊缝金属内AF晶粒形核以及长大行为的影响规律.?结果表明,在大热输入焊接条件下,...
|
| 关 键 词： | 大热输入 焊缝金属 针状铁素体 晶粒取向 |
| 收稿时间： | 2020-09-29 |
Study on grain growth behavior of acicular ferrite in weld deposited metal |
| |
| Affiliation: | 1.Longyan University, Longyan, 364012, China2.Xinyu University, Xinyu, 338004, China3.Shandong Heng Yuan Weapon Technology CORP., LTD, Taian, 271000, China4.Quzhou Quality and Technical Supervision and Testing Center, Quzhou, 324000, China5.Institute for Experimental Molecular Imaging, RWTH Aachen University, Aachen, 52074, Germany |
| |
| Abstract: | In this study, having acicular ferrite (AF) as the matrix the high heat input weld metal was taken as the research object and acicular ferrite (AF) grain orientation relationships (ORs) in the deposited metal was identified from Metallographic microscope (OM), electron bacK-Scatter diffraction device (EBSD), automatic static phase change instrument, etc, the influence of different heat input on the growth behavior of AF grain in the weld metal was analyzed. The results showed that, When the cooling rate of the weld metal is below the critical rate, AF in the weld metal nucleated from the inclusions with polygonal ferrite morphology, and deviated from K-S OR with respect to parent phase γ. When the temperature of the deposited metal decreased to the transformation start temperature, AF grew up with slender needle morphology, and exhibited K-S OR with respect to parent phase γ. However, with the decrease of the welding heat input, AF nuclear size reduced, and the approach to K-S OR with respect to parent phase γ was accelerated, when the cooling rate of the weld metal exceeds the critical rate, AF grains can grow rapidly without nucleation. |
| |
| Keywords: | |