水雾化制备FeSiCr软磁粉末磁性能研究 |
| |
引用本文: | 孟令兵,于海琛,吕世雅,江忠民,麻洪秋,关立东. 水雾化制备FeSiCr软磁粉末磁性能研究[J]. 粉末冶金技术, 2021, 39(4): 345-349. DOI: 10.19591/j.cnki.cn11-1974/tf.2021060008 |
| |
作者姓名: | 孟令兵 于海琛 吕世雅 江忠民 麻洪秋 关立东 |
| |
作者单位: | 1.安泰(霸州)特种粉业有限公司,霸州 065701 |
| |
基金项目: | “科技助力经济2020”重点专项资助项目(SQ2020YFF0422974) |
| |
摘 要: | 采用水雾化工艺制备FeSiCr软磁合金粉末,经筛分合批后制成粒径(D50)5~40μm的样品.研究了不同粒径FeSiCr软磁粉末对磁性能的影响,为产品应用提供指导性实验.研究结果表明,随着粉末粒径的增大,粉心的磁导率逐渐增大,在100~1000 kHz的频段范围内,磁导率衰减幅度小于5%,具有较好的频率特性.随着粉末粒...
|
关 键 词: | 水雾化 FeSiCr软磁粉末 有效磁导率 损耗 直流偏置 |
收稿时间: | 2021-06-12 |
Study on magnetic properties of FeSiCr soft magnetic powders prepared by water atomization |
| |
Affiliation: | 1.Advanced Technology (Bazhou) Special Powder Co., Ltd, Bazhou 065701, China2.Special Powder Atomization Technology Innovation Center of Hebei Province, Bazhou 065701, China |
| |
Abstract: | The FeSiCr soft magnetic alloy powders were prepared by water atomization, and the powders with the particle size (D50) between 5 and 40 μm were obtained. Effect of particle size on the magnetic properties of the FeSiCr soft magnetic alloy powders was studied to provide the guidance for the products application. In the results, the effective permeability (μe) of the FeSiCr alloy powders increases with the increase of particle size, the attenuation amplitude of permeability is less than 5% in the frequency range of 100~1000 kHz, showing a good stability with frequency. Futhermore, with the increase in the particle size of FeSiCr alloy powders, the direct current (DC) bias properties decrease, and the core losses deteriorate, in which the increased losses is mainly due to the eddy current losses inside the particles of FeSiCr alloy powders. |
| |