| 铸钢轧辊电火花沉积WC-4Co涂层组织和性能分析 | |
| 引用本文： | 王建升,孟惠民,张瑞珠,严大考.铸钢轧辊电火花沉积WC-4Co涂层组织和性能分析[J].焊接学报,2010,31(10):43-46. |
| 作者姓名： | 王建升 孟惠民 张瑞珠 严大考 |
| 作者单位： | 1. 华北水利水电学院机械学院,郑州,450011;北京科技大学,材料科学与工程学院,北京,100083 2. 北京科技大学,材料科学与工程学院,北京,100083 3. 华北水利水电学院机械学院,郑州,450011 |
| 基金项目： | 水利部948推广项目，中国科技部国际科技合作项目 |
| 摘 要： | 采用新型电火花沉积设备,把陶瓷WC-4Co电极材料沉积在铸钢轧辊材料上,制备了WC-4Co沉积涂层,研究了其微观组织及耐磨性能.结果表明,沉积层主要由Fe3W3C,Co3W3C,Fe和SiC等相组成;沉积层与基体呈冶金结合,过渡层组织主要是柱状晶结构组织;Fe3W3C和Co3W3C等硬质相弥散分布于沉积层Fe基体上,部分区域硬质相达到了纳米颗粒尺寸;沉积层硬度的平均硬度为1617.2HV;沉积层较铸钢轧辊的磨损性能提高了2.1倍,沉积层的磨损机理主要是粘着磨损、疲劳磨损、氧化磨损和磨粒磨损的综合作用,细小的弥散分布的硬质相是沉积层硬度及耐磨性提高的主要因素. |
| 关 键 词： | 电火花沉积 铸钢轧辊 组织结构 耐磨性 |
| 收稿时间： | 2009/5/11 0:00:00 |
Microstructure and properties of WC-4Co ESD coating of cast steel roll |
|
| WANG Jiansheng,MENG Huimin,ZHANG Ruizhu and YAN Dakao.Microstructure and properties of WC-4Co ESD coating of cast steel roll[J].Transactions of The China Welding Institution,2010,31(10):43-46. | |
| Authors: | WANG Jiansheng MENG Huimin ZHANG Ruizhu and YAN Dakao |
| Affiliation: | North China Institute of Water Conservancy and Hydroelectric Power, Zhengzhou 450011, China;College of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China,College of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China,North China Institute of Water Conservancy and Hydroelectric Power, Zhengzhou 450011, China and North China Institute of Water Conservancy and Hydroelectric Power, Zhengzhou 450011, China |
| Abstract: | WC-4Co electrode material is deposited on the surface of cast steel roll by electro-spark deposition(ESD).The microstructure and wear resistance of the coating are investigated.The results show that the coating consists of Fe3W3C,Co3W3C,Fe and SiC phases,and the coating bonded with cast steel roll substrate is well metallurgical.The phases of Fe3W3C and Co3W3C distribute dispersedly in the coating with the extra-fine structure.The average hardness of the coating is 1 617.2 HV.The resistance performance of the coating is 2.1 times higher than that of the cast steel substrate.The wear mechanism is adhesion wear,fatigue wear,oxidization wear and abrasive wear,but the main wear mechanism is fatigue wear and abrasive wear. |
| Keywords: | WC-4Co |