Structural changes of glass-ceramics of the Cu2O-Al2O3-SiO2 system on heating in air

The behaviour of copper ions in low thermal expansion glass-ceramics prepared from Cu₂O · Al₂O₃ ·_nSiO₂ glasses, or in-spodumene type Cu₂O · Ae₂O₃ ·nSiO₂ crystals included in the glass-ceramics on heating in air was investigated. On hewing at 300 to 500° C, the copper ions behaved as in the corresponding glasses. Cuprous ions in the glass-ceramics or-spondumene type crystals were oxidized into the cupric state, and at the same time an equal amount of cuprous ions to those oxidized were expelled out of the specimen for the requirement of electrical charge neutrality and then reacted with oxygen to form CuO on the surface. The oxidation of cuprous ions and the decrease of the copper content of the-spondumene type crystals brought about a considerable decrease in the lattice spooings.