Grain refinement in magnetically stirred GTA welds of aluminum alloys

The mechanisms of grain refinement have been examined for magnetically stirred gas tungsten arc (GTA) welds completely penetrating thin sheets of several aluminum alloys. Grain refinement in unstirred welds may be brought about by adding sufficient titanium to produce heterogeneous nucleation by Ti-rich particles. In some alloys magnetic stirring is shown to extend the range of welding conditions which produce a partially equiaxed structure, and to widen the equiaxed fraction of partially equiaxed welds. This is attributed to magnetic stirring lowering the temperature gradient, allowing nucleation and growth of Al-rich grains further ahead of the columnar interface growing in from the fusion boundaries. In alloys with low Ti levels, magnetic stirring may cause refinement by sweeping grains from the partially molten zone ahead of the advancing solidification interface. This mechanism requires that the partially molten zone be sufficiently wide, and that the grain size in this zone remain small.