Compressive Properties and Curing Behaviour of Unsaturated Polyester Resins in the Presence of Vinyl Ester Resins Derived from Recycled Poly(ethylene terephthalate) |
| |
Authors: | Ayman M Atta Sayed I Elnagdy Manar E Abdel-Raouf Shimaa M Elsaeed Abdel-Azim A Abdel-Azim |
| |
Affiliation: | (1) Egyptian Petroleum Research Institute, Nasr City, Cairo, 11727, Egypt;(2) Chemistry Department, Faculty of Science, Ain Shams University, Abasia, Cairo, Egypt |
| |
Abstract: | Poly(ethylene terephthalate) waste was depolymerised in the presence of tetraethylene glycol and manganese acetate as a catalyst, so as to produce oligomers. An epoxy resin was then prepared by the reaction of these oligomers with epichlorohydrin in presence of NaOH as a catalyst. New diacrylate and dimethacrylate vinylester resins were then synthesized by reaction of the terminal epoxy groups with acrylic and methacrylic acid in the presence of triphenyl phosphite as a catalyst. The chemical structures of the resulting vinyl ester resins were confirmed by 1HNMR. The vinyl ester resins were used as crosslinking agents for unsaturated polyester resin diluted with styrene, using free radical initiator and accelerator.
The curing behaviour of the unsaturated polyester resin, vinyl ester resins and styrene was evaluated at temperatures from 25 to 55 ○C. The compression properties of the cured resins, having different vinyl ester contents and different cure temperatures, were evaluated. Increasing the cure temperature and the vinyl ester content led to a pronounced improvement in the compression strength and Young’s modulus. |
| |
Keywords: | curing behaviours epoxy resins mechanical characteristics poly(ethylene terephthalate) recycling unsaturated polyesters |