Surface Energetics and Adhesion

The relationships between surface energetics and adhesion are critically reviewed. New data that confirm such relationships, for peel tests as well as lap shear tests, are presented. The effect of hydrothermal aging of aluminum surfaces on surface energetics can be used to predict degradation in bond strength. The mechanism of failure for elastic adhesives (such as Scotch ® tape) in peel tests may be essentially the same as for more brittle adhesives (such as epoxies) in lap shear tests. This mechanism may involve brittle fracture that forms a critical flaw at the adherend-adhesive interface (on a microscopic level), followed by crack propagation which then may include considerable elastic and plastic deformation. The locus of propagation (fractography) is generally not (but may be) relevant to the problem of how to remedy mechanical weakness in an adhesive joint, since the local region of critical flaw formation rather than the general surface area determines the joint strength.