Corrosion Behavior of Mg65Cu25-xZnxGd10 （x=0, 5）Metallic Glass

The effect of substitutional element Zn on corrosion behavior of Mg65Cu25Gd10 glass was investigated. The amorphous structure of Mg65Cu25-xZnxGd10 （x=0,5） alloys were examined by X-ray diffractometry and differential scanning calorimetry （DSC）. The dissolution rates of Mg65Cu25-xZnxGd10 （x=0, 5） metallic glasses in a 5 wt% NaCl solution with pH value of 7 were determined by a hydrogen evolution testing method. The corrosion behavior of these alloys was characterized using dipping tests with 5 wt% NaCl, in combination with electrochemical measurements and scanning electron microscopy （SEM）. Results show that the anti-corrosion ability of Mg65Cu25Gd10 alloy is significantly improved due to the addition of Zn. Possible mechanism responsible for the improvement is discussed.