| 凝固末端电磁搅拌对77B铸坯中心偏析的影响 |
| |
| 引用本文： | 戴秀东,李俊. 凝固末端电磁搅拌对77B铸坯中心偏析的影响[J]. 山西冶金, 2009, 32(2): 29-31 |
| |
| 作者姓名： | 戴秀东 李俊 |
| |
| 作者单位： | 山西太钢不锈钢股份有限公司,山西,太原,030003 |
| |
| 摘 要： | 77B铸坯在拉拔过程中常因塑性不足而发生拉断。通过电镜、低倍等对断裂的机理进行分析，最终确定使用凝固末端电磁搅拌器来消除铸坯的中心偏析。结果表明，经过末端电磁搅拌的连铸坯试样中心偏析程度基本上得到了改善，取得了较好的效果。
|
| 关 键 词： | 凝固末端电磁搅拌 77B 中心偏析 |
Effects on 77B Cast Slab Center Segregation of F-EMS |
| |
| DAI Xiudong,LI Jun. Effects on 77B Cast Slab Center Segregation of F-EMS[J]. Shanxi Metallurgy, 2009, 32(2): 29-31 |
| |
| Authors: | DAI Xiudong LI Jun |
| |
| Affiliation: | Shanxi Taigang Stainless Steel Co.Led.;Taiyuan 030003;Chian |
| |
| Abstract: | 77B cast slabs always fracture because of poor plasticity in drawing course.Analysing fracture mechanics by low power and electronic microscope,thought cast slabs have severity center segregation,so want to erase the flaws by F-EMS.The results showed that slab center carbon segregation was reduced obviously by low power and chemical constitution analysis at F-EMS and no F-EMS,therefore resolved fracture problem. |
| |
| Keywords: | 77B |