| 氧化铜为助熔剂制备硼酸铝晶须 |
| |
| 引用本文： | 田阳,刘宇舟,王东,张亮,谭宏斌. 氧化铜为助熔剂制备硼酸铝晶须[J]. 陶瓷, 2011, 0(21): 20-21 |
| |
| 作者姓名： | 田阳 刘宇舟 王东 张亮 谭宏斌 |
| |
| 作者单位： | 陕西理工学院材料学院,陕西汉中,723000 |
| |
| 摘 要： | 利用H3BO3和Al（OH）3为原材料，CuO为助熔剂制备硼酸铝9Al2O3·2B2O3晶须。经研究发现，试样在1350℃煅烧6h，试样的物相为硼酸铝相。以CuO为助熔剂制备的硼酸铝晶须，其直径较均匀为1～5μm，长度为10μm。
|
| 关 键 词： | 助熔剂 硼酸铝 晶须 形貌 |
Preparation of Aluminum Borate by Using Copper Oxide as Fusing Agent |
| |
| Tian Yang,Liu Yuzhou,Wang Dong,Zhang Liang,Tan Hongbin. Preparation of Aluminum Borate by Using Copper Oxide as Fusing Agent[J]. Ceramics, 2011, 0(21): 20-21 |
| |
| Authors: | Tian Yang Liu Yuzhou Wang Dong Zhang Liang Tan Hongbin |
| |
| Affiliation: | (School of Materials Science and Engineering, Shaanxi University of Technology, Shaanxi, Hanzhong, 723000) |
| |
| Abstract: | The aluminum borate （9Al2O3·2B2O3 ） whiskers was prepared by using Al（OH）3 and H3BO3 as raw materials, CuO as fusing agent. The resulted indicated aluminum borate was obtained by sintering sample at 1 350℃ for 6 h. The aluminum borate whiskers were obtained with 1-5μm in diameter, 10μm in length. |
| |
| Keywords: | Fusing agent Aluminum borate Whiskers Morphology |