Novel Fabrication Route to Al2O3–TiN Nanocomposites Via Spark Plasma Sintering

A novel method for the preparation of Al₂O₃–TiN nanocomposites was developed. A mixture of TiO₂, AlN, and Ti powder was used as the starting material to synthesize the Al₂O₃–TiN nanocomposite under 60 MPa at 1400°C for 6 min using spark plasma sintering. X-ray diffractometry, scanning electron microscopy, and transmission electron microscopy were used for detailed microstructural analysis. Dense (up to 99%) nanostructured Al₂O₃–TiN composites were successfully fabricated, the average grain size being less than 400 nm. The fracture toughness ( K _{I C} ) and bending strength (σ_b) of the nanostructured Al₂O₃–TiN composites reached 4.22±0.20 MPa·m^1/2 and 746±28 MPa, respectively.