| Stress Analysis of CaO-Al_2O_3-SiO_2 System Glass-ceramic with Different Thickness |
| |
| 引用本文： | 程金树,谢俊. Stress Analysis of CaO-Al_2O_3-SiO_2 System Glass-ceramic with Different Thickness[J]. 武汉理工大学学报(材料科学英文版), 2005, 0(4) |
| |
| 作者姓名： | 程金树 谢俊 |
| |
| 作者单位： | Key Lab of Silicate Materials Science and Engineering Ministry of Education，Wuhan University of Technology Wuhan 430070 China，Key Lab of Silicate Materials Science and Engineering Ministry of Education，Wuhan University of Technology Wuhan 430070 China |
| |
| 基金项目： | FundedbytheNationalNaturalScienceFoundationofChina(No.50272043) |
| |
| 摘 要： | 1Introduction Themaincrystallinephaseofarchitecturaldecoratedglass ceramicisβwollastonite.WiththedevelopmentofCASglass ceramicindustry,therearesomeintractableproblemsintheindustryprocess,suchastransmogrifica tionorburst.Theemergenceoftheseproblemscandeep…
|
Stress Analysis of CaO-Al_2O_3-SiO_2 System Glass-ceramic with Different Thickness |
| |
| Abstract: | In order to study the relationship between thickness and residual stress in CaO-Al_2O_3-SiO_2 glass-ceramics.The residual stress was measured in CaO-Al_2O_3-SiO_2 system glass-ceramic with different thickness,and the formation mechanism and characterization of residual stress in CAS system Glass-ceramic were analyzed by the X-ray diffraction analysis. The experimental results show the compressive residual stress increases with thickness of glass-ceramic increasing |
| |
| Keywords: | glass-ceramics residual stress CaO-Al_2O_3-SiO_2 system |