Evaluation of white rot decay in phenol-formaldehyde resin treated European beech (Fagus sylvatica L.) LVL by drilling resistance measurements

Improving the properties of laminated veneer lumber (LVL) through wood modification expands its usage as building material, especially for outdoor applications. The outdoor performance of LVL products needs to be tested against different biotic agents, and methods are needed for testing and evaluating their effect on the structural integrity of LVL. In this study, drilling resistance (DR) measurements were used to quantify the effect of fungal decay in phenol-formaldehyde (PF) resin treated European beech (Fagus sylvatica L.) LVL caused by white rot fungi. Material specific peculiarities and their effect on the evaluation method were studied such as the effect of drill bit blunting, moisture content (MC), drilling direction and PF resin content on the DR of PF-modified LVL. The drilling direction in relation to veneer and glue layers had a significant effect on DR and feeding resistance (FR). The PF resin treatment increased the DR. Feeding resistance was found more sensitive to the blunting of the drill bit than DR. The effect of MC on DR and FR was found to be insignificant. The effect of PF resin content on the prediction of mass loss (ML) by DR became prominent only for ML by white rot decay below 10 %. Correlations between DR, ML due to fungal decay and weight percent gain were established and described with a two-factor regression model. The drill bit feed rate of 0.5 m min^?1 and the rotational frequency of 3500 min^?1 as well as the transversal drilling in relation to the veneer (glue) layers were recommended for the assessment of beech LVL treated with PF resin. The DR measurements showed high potential as a fast standard evaluation method for decay and strength loss of LVL products.